Fabrication and study the performance of solar cell made from new nanostructure phthalocyanine complex thin film Fabrication and study the performance of solar cell made from new nanostructure phthalocyanine complex thin film |
|
الموضوع |
: |
physics |
|
لغة الوثيقة |
: |
الانجليزية |
|
المستخلص |
: |
Nanocrystalline thin film of 2,3,9,10,16,17,23,24-octa(n-hexyl) phthalocyaninatoruthenium(II), [(n-hexyl)
(8)PcRu] deposited under high vacuum by thermal evaporation technique. The surface morphology of
[(n-hexyl)(8)PcRu] thin film was measured using transmission electron microscopy (TEM) which
showed nano-rod structures. The current-voltage (I-V) and capacitance-voltage (C-V) measurements of
[(n-hexyl)(8)PcRu] onto p-Si substrate were studied. Dark current voltage (I-V) measurement was
investigated at different temperatures ranging from 308 to 378 K indicates two conduction mechanisms:
the first at lower forward voltages thermionic emission and second at higher forward voltages space
charge limited currents (SCLC) with a single trap level. The ideality factor, n, series resistance R-s,
shunt resistance, R-sh, and barrier height, Phi(b), were determined. The study of reverse voltage bias
was interpreted in terms of generation-recombination. Abrupt nature was observed from dependence of
capacitance-voltage for the device. Photovoltaic behavior was exhibited with power conversion
efficiency eta of 2.1%. |
|
ردمد |
: |
0379-6779 |
|
اسم الدورية |
: |
SYNTHETIC METALS |
|
المجلد |
: |
199 |
|
العدد |
: |
10 |
|
سنة النشر |
: |
1435 هـ
2015 م |
|
نوع المقالة |
: |
مقالة علمية |
|
تاريخ الاضافة على الموقع |
: |
Tuesday, August 22, 2017 |
|
الباحثون
| A.A Hendi | Hendi, A.A | باحث رئيسي | دكتوراه | |
| EFM El-Zaidia, | El-Zaidia,, EFM | باحث مشارك | دكتوراه | ad_eman@hotmail.com |
|