Zn- and O-polar surface effects on Raman mode activation in homoepitaxial ZnO thin films
Zn- and O-polar surface effects on Raman mode activation in homoepitaxial ZnO thin films
 
الموضوع : physics 
لغة الوثيقة : الانجليزية 
المستخلص : ZnO thin films were grown by metalorganic chemical vapor deposition on (0001) Zn- and O-polar surfaces of ZnO substrate. The surface morphology of these films was investigated by micro-Raman scattering and scanning electron microscopy. In the case of Zinc-polar face and using back scattering configuration, two new Raman bands were observed at 398 and 584.5 cm(-1). They have been interpreted as quasi phonons TO (qTO) and LO (qLO) respectively. The origin of these modes was attributed to the particular morphology of ZnO films grown on Zn-polar face, which consists in c-axis nano-platelets, randomly tilted from the substrate. qTO and qLO frequencies have been calculated using the model of Loudon. SEM observation is in agreement with our Raman interpretation 
ردمد : 0038-1098 
اسم الدورية : SOLID STATE COMMUNICATIONS 
المجلد : 152 
العدد : 9 
سنة النشر : 1433 هـ
2012 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Tuesday, July 25, 2017 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
A Souissi,Souissi,, A باحث رئيسيدكتوراهahmed_souissi@hotmail.fr
C Sartel,Sartel,, C باحث مشاركدكتوراه 
A MeftahMeftah, A باحث مشاركدكتوراه 
A Lusson,Lusson,, A باحث مشاركدكتوراه 
P GaltierGaltier, P باحث مشاركدكتوراه 
V SalletSallet, V باحث مشاركدكتوراه 
M (Oueslati(Oueslati, M باحث مشاركدكتوراه 

الملفات

اسم الملفالنوعالوصف
 42250.pdf pdf 

الرجوع إلى صفحة الأبحاث